Study the effect of calcination temperature on physical and magnetic properties of bare cobalt nanoparticles and that coated with silica shell

Abstract

In this paper, in order to investigation the effect of calcination temperature on the structural and magnetic properties of cobalt nanoparticles, samples have been prepared by Co-precipitation method at different calcination temperature. Cobalt nanoparticles have been prepared by Co-precipitation method at room temperature using hydrazine as reducing in ethanol hydrazine alkaline environment. This agent reduces cobalt salts to Cobalt nanoparticles in FCC and HCP phases. Phase analysis and investigation of Structural properties of the samples using X-ray diffraction patterns (XRD) confirm the formation of hexagonal phases of Co nanoparticles. Transmission electron microscopy (TEM) was used for determining the size and shape morphology of nanoparticles. Magnetic properties of these nanoparticles have been investigated using a Vibrating sample magnetometer (VSM). The results indicate that these nanoparticles are ferromagnetic at room temperature. In addition, in this paper Co nanoparticles coated with silica shell have been prepared by the wet chemical method. TEM images showed the cobalt core with average diameter of 17-20 nm coated by a silica shell with thickness of 5-7nm. Hysteresis Loop of these Co nanoparticles coated by silica shell illustrates 16.9 emu/gr for saturation magnetization at 10000 (Oe), which is much less than that of Cobalt nanoparticles

Keywords

References

[1] M.L.Wagner, L.D. Schmidt, J. Phys. Chem. 99 (1995) 805.

[2] S.W. Moore, Sol. Energy Mater. 12 (1985) 435.

[3] M. Ozaki, Mater. Res. Soc. Bull. 14 (1989) 35.

[4] F. Guo, H. Zheng, Z. Yang, Y. Qian, J. of Materials Letters 56 (2002) 906–909.

[5] Y. Zhu, H. Zheng, Q. Yang, A. Pan, Z. Yang, Y. Qian, J. of Crystal Growth 260 (2004) 427–434.

[6] V.F. Puntes, K.M. Kishnan, A.P. Alivisatos, Science 291 (2001) 2115.

[7] D.P. Dinega, M.G. Bawendi, Angew. Chem. Int. Ed. Engl. 38 (1999) 1788.

[8] X.L. Dong, C.J. Choi, B.K. Kim, Scripta Mater. 47 (2002) 857.

[9] C. J. Fernandez , D. Niznansky, N. Viart, J. L. Rehspringer, J. Sol-Gel Sci. Technol. 8 (1997) 615.

[10] J. F. Loffler, H. B. Braun, W. Wagner, G. Kostorz, A. Wiedenmann, Mater. Sci. Eng. A 304 (2001) 1050.

[11] Y. D. Zhang, J. I. Budnick, W. A. Hines, S. A. Majetich, E. M. Kirkpatrick, Appl. Phys.Lett. 76 (2000) 94.

[12] Y. D. Zhang, S. H. Wang, D. T. Xiao, US Patent Appl. No. 60 (2000) 243649.

[13] V. Salgueirino-Maceira, M. Correa-Duartec, J. Mater. Chem 16 )2006 (3593–3597.

[14] Y. Kobayashi, M. Horie, M. Konno, B. Rodriguez-Gonzalez, L. M. Liz-Marzan, J. Phys. Chem. B 107 (2003) 7420-7425.

[15] A.S. Eggeman, A.K. Petford-Long, P.J. Dobson, J. Wiggins, T. Bromwich, R. Dunin-





Borkowski, T. Kasama, J. of Magnetism and Magnetic Materials 301 (2006) 336–342.

[16] V. Salgueirino-Maceira , M. Correa-Duartec, A. Huchtd, M. Farled. J. of Magnetism and Magnetic Materials 303 (2006) 163–166.

[17] D.H. Qin, L. Cao, Q.Y. Sun, Y. Huang, H.L. Li, Chem. Phys. Lett. 358 (2002) 484.

Files

History

  • Receive Date: 02 July 2025
  • Revise Date: 04 February 2026
  • Accept Date: 02 July 2025

Share

How to cite

Statistics